Hebei Hongkuo Trading Co., Ltd.

DESCRIPTION UHP graphite electrode is used for the recycling of steel in the electric arc furnace industry. Its main ingredient is high-value needle coke which is made from either petroleum or coal tar. Graphite electrodes are finished with a cylinder shape and machined with threaded areas at each end. In this way, the graphite electrodes can be assembled into an electrode column using electrode nipple. In order to meet the requirement of higher work efficiency and lower total cost, large capacity ultra-high power arc furnaces are becoming more and more popular. Because of this, UHP graphite electrodes with diameters of over 500 mm will dominate market. FEATURE Withstand large currents, high discharge rate.Good dimension stability, not easy to deform.Resistant to cracking & spalling.High resistance to oxidation and thermal shock.High mechanical strength, low electrical resistance.High machining accuracy, good surface finishing. APPLICATION Graphite electrodes are widely used for production of alloy steels, metal and other nonmetallic materials, etc.DC electric arc furnace.AC electric arc furnace.Submerged arc furnace.Ladle furnace. SPECIFICATION Table 1: Technical Specification of UHP Graphite Electrode Resistance Density FlexureStrength ElasticModulus AshContent CTE CurrentLoad CurrentDensity (inch) (≤,µΩ·m) (≥,g/cm3) (≥,MPa) (≤,GPa) (≤,%) (100°C–600°C) (A) (A/cm2) (≤,10-6/°C) 10 14 8100–12200 20–30 12 14 15000–22000 20–30 14 14 20000–30000 20–30 16 14 25000–40000 19–30 18 14 32000–45000 19–27 20 11 14 38000–55000 18–27 22 11 14 42000–66000 17–26 24 11 14 49000–76000 17–26 Table 2: Graphite Electrode Size & Tolerance Diameter(mm) Length(mm) NominalDiameter ActualDiameter NominalLength Tolerance ShortLength (inch) (mm) (max.) (min.) (roughspot) 10 250 256 251 248 1600/1800 ±100 -275 12 300 307 302 299 1600/1800 14 350 357 352 349 1600/1800 16 400 409 403 400 1600/1800/2000/2200 18 450 460 454 451 1600/1800/2000/2200 20 500 511 505 502 1800/2000/2200/2400 22 550 562 556 553 1800/2000/2200/2400 24 600 613 607 604 2000/2200/2400/2700 SURFACE QUALITY There should be less than two defects or holes on the electrode surface, the maximum size of which is mentioned in the below chart.There should be no transverse crack on the electrode surface. For the longitudinal crack, the length should be less than 5% of the electrode circumference and the width should be 0.3 to 1.0 mm.The width of black area on electrode surface should be less than 1/10 of the electrode circumference and the length should be less than 1/3 of the electrode. SpecificationDefectDimension NominalDiameterofGraphiteElectrode(mm) 300–400 450–600 Diameter(mm) 20–40 30–50 (<20mmshouldbenegligible) (<30mmshouldbenegligible) Depth(mm) 5–10 10–15 (<5mmshouldbenegligible) (<10mmshouldbenegligible) Guidance of Using Being hard and brittle ,artificialgraphite electrode shall be specially handled.Proper operationg may reduce the consumption and cost. 1. Professional tools should be used for hoisting graphite electrodes. It is strictly forbidden to use a crowbar to prevent impact damage during handling. 2. Graphite electrodes are prohibited from rain, snow and water, and should be kept dry. If it is found to be damp, it should be dried before use, the temperature should not exceed 100 ºC, and the drying time should not be less than 48h. 3. Do not stack near debris such as clay, slag, etc., so as not to pollute the surface of the graphite electrode and affect the conductive effect. 4. Before the graphite electrode is connected, carefully check whether the electrode connector hole is intact, whether the connector thread is damaged, and whether the connector bolt is lost. When the electrode is lifted, the electrode connector thread of the ground terminal should be prevented from being damaged. 5. Dust and debris in the joints and joint holes should be blown dry with compressed air. 6. Graphite electrodes must be tightly connected, and no tilt is allowed during connection. Torque wrenches should be used to prevent excessive force or too small, and the gap is not greater than 0.4mm. 7. The electrode holder should be clamped, not loose and in good contact, and no arc should be generated. Otherwise, the connection will be reddish, oxidized, thinned and broken. 8. If the electrode is lifted with a metal lifting plug, the thread in the joint hole must not be damaged. After lifting, the lifting plug should be unscrewed to prevent dust and debris from falling into the joint hole. 9. When the electrode lifting device of the electric furnace is running, it should be kept stable. After the furnace cover is repaired, check whether the furnace cover is positioned correctly. During smelting, refractory materials are used to close the furnace lid to prevent the oxidation of the upper electrode of the flame in the furnace. 10. The holder should be clamped outside the safety wire of the electrode connector hole area. 11. When distributing the molten pool, the big piece is at the bottom and the small piece is at the top. Do not place the charge with poor conductivity on the top. During melting, the unmelted charge should be handled in time to prevent the collapsed material from breaking the electrode.